EVA resin is a mixture composed of polymerization molecules of different chain lengths and chain structures. Compared with polyethylene, the ethylene acetate monomer is introduced in the molecular chain, which reduces the crystallinity, improves the flexibility and impact resistance, and improves the packing mixing and thermal sealing. In a wide temperature range has good softness, impact resistance, resistance to environmental stress and good optical properties, with the different content of ethylene acetate in EVA copolymer and melting index, physical properties, chemical properties and processing properties are also different, so it can be widely used in various fields.
project | 2022(EVA14-2) | Y2045(EVA18-3) | Y2013 | |||
nominal value | specifications | nominal value | specifications | nominal value | specifications | |
Melt mass flow rate (MFR), g / 10min | 2.0 | 1.6~2.4 | 2.9 | 2.4~3.5 | 1.5 | 1.2~1.8 |
The vinyl acetate content,% | 14.0 | 12.0~16.0 | 18.0 | 16.0~19.5 | 18.0 | 16.5~19.5 |
Note: The table is the main indicators, and the detailed indicators see the enterprise standard Q / HG 013 0120
(1) Film processing type- -agricultural film, food soft packaging film, tensile film, casting film, heavy packaging film, hot melt film, etc.
(2) Injection molding products- -hollow products, foam sheet, flexible hose, low-temperature resistant gasket, fender, etc.
(3) Hot melt adhesive type- -all kinds of hot melt adhesives, coatings, etc.
(4) Other- -wire, cable materials, medical equipment, laminating materials.
25kg paper-plastic composite packaging bag packaging
EVA resin shall not be exposed to the sun or rain, shall not be mixed with sand, broken metal, coal and glass, etc., and shall not be mixed with toxic, corrosive or flammable materials. Use sharp tools like hooks during loading and unloading shall not be used to damage the packing bag. It should be stored in a clean, cool, dry and ventilated warehouse, away from heat source and prevent direct sunlight. If stored outdoors, cover it with a tarpaulin.